RESEARCH ON ADSORPTION OF Cd( Ⅱ) BY EDTA INTERCALATED HYDROTALCITE

摘要: 采用共沉淀的方法合成了镁铝水滑石和EDTA插层水滑石,并对两者进行表征分析,同时比较分析了EDTA插层水滑石和镁铝水滑石对Cd2+的吸附效果及影响因素,确定了合成高吸附容量的EDTA插层水滑石的最佳条件和其吸附镉的最佳吸附条件。结果表明:p H值为12、晶化时间为1 h和水浴温度为50℃是插层水滑石最佳合成条件;吸附剂投加量为1.0 g/L、时间为50 min、p H值为6、温度为50℃是插层水滑石吸附Cd2+的最佳条件。

Abstract: Adopting the method of coprecipitation，magnesium aluminum hydrotalcite and EDTA intercalated hydrotalcite was compounded． The paper compared and analyzed EDTA intercalated hydrotalcite and magnesium aluminum hydrotalcite on the adsorption of Cd2 + and influence factors，obtained the best synthesis conditions of EDTA intercalated hydrotalcite and the best adsorption conditions． Results showed that the best synthesis conditions of EDTA intercalated hydrotalcite were: pH of 6，time of 1h， temperature of 50 ℃ and the best adsorption conditions were: Adsorbent additive amounts of 1. 0 g /L，time of 50 min， pH of 6，temperature of 50 ℃．

1.	陈振宇，肖春艳，刘宏. 淀粉/三维磁性氧化石墨烯的制备及其对Cd(Ⅱ)的吸附性能和机理. 环境工程学报. 2023(07): 2130-2144 . 百度学术
2.	孟梅，勇志华，张大可，苟乐乐，周玲. 多级结构材料制备的研究进展. 化工技术与开发. 2023(09): 35-38 . 百度学术
3.	郑秀君，江欣悦，李木子，赵冬梅，初小宇. 改性水滑石/聚乙烯醇复合膜的制备及性能. 化学试剂. 2022(01): 65-72 . 百度学术
4.	吴青山，赵鹏程，刘志启，周自圆，李娜，莫云泽. 镁铝水滑石的制备与应用研究. 材料导报. 2022(S1): 149-156 . 百度学术
5.	张爽，丁欣欣，闫良国. 改性水滑石类材料的制备及其吸附性能研究进展. 中国粉体技术. 2021(01): 1-10 . 百度学术
6.	李木子，郑秀君，任德财. 焙烧复原法制备山梨酸和苯甲酸插层水滑石及其缓释性能研究. 化学试剂. 2021(05): 610-616 . 百度学术
7.	许昶雯，王国英，刘吉明，岳秀萍，宁舒怡. 制备焙烧Mg/Al水滑石及同时去除水中氟和硬度. 华侨大学学报(自然科学版). 2018(05): 706-713 . 百度学术